Corrosion atlas : : a collection of illustrated case histories /\ compiled by Evert D.D. During.
|
| Edition Statement
|
:
|
Third, expanded and revised edition.
|
| Publication Statement
|
:
|
Amsterdam, Netherlands ;Cambridge, MA :: Elsevier,, [2018]
|
|
|
:
|
, ©2018
|
| Page. NO
|
:
|
1 online resource
|
| ISBN
|
:
|
0128185554
|
|
|
:
|
: 1523121963
|
|
|
:
|
: 9780128185551
|
|
|
:
|
: 9781523121960
|
|
|
:
|
0444642692
|
|
|
:
|
9780444642691
|
| Bibliographies/Indexes
|
:
|
Includes bibliographical references.
|
| Contents
|
:
|
Front Cover; Corrosion Atlas: A Collection of Illustrated Case Histories; Corrosion Atlas: A Collection of Illustrated Case Histories; Copyright; Dedication; CONTENTS; FOREWORD; Preface; ACKNOWLEDGMENTS; USER GUIDE FOR THE CORROSION ATLAS; CLASSIFICATION OF THE CASE HISTORIES*; PHENOMENA INDEX IN ALPHABETIC ORDER; SYSTEMS INDEX; A: General information; INTRODUCTION; Part I: General Aspects of Corrosion, Corrosion Control, and Corrosion Prevention; 1. DEFINITION OF CORROSION; 2. THE CONSEQUENCES OF CORROSION; Technical Consequences; Economic Consequences; Social Consequences.
|
|
|
:
|
3. THE THEORY OF ELECTROCHEMICAL CORROSIONOxidation and Reduction; Polarization and Depolarization; The Corrosion Potential; The E/pH Diagram (Pourbaix Diagram); Corrosion Rate and Polarization Diagrams; Closing Remarks; 4. FORMS OF ELECTROCHEMICALCORROSION; Uniform Corrosion; Localized Corrosion; 5. FAILURE ANALYSIS AND DIAGNOSIS; 6. CORROSION CONTROL; 7. CORROSION PREVENTION AT THEDESIGN STAGE; General; Factors Influencing Selection of Materials and Corrosion Resistance; Design Rules; Part II: Corrosion Topics; 1. CAVITATION DAMAGE; Occurrence; Prevention; 2. EROSION CORROSION; Occurrence.
|
|
|
:
|
9. MICROBIOLOGICALLY INDUCED CORROSIONCorrosion Phenomena; Corrosion of Carbon Steel by SRB; Corrosion of Stainless Steel by Iron Bacteria; Identification of MIC; 10. PITTING AND CREVICE CORROSIONOF STAINLESS STEEL; Crevice Corrosion; 11. SELECTIVE LEACHING; Dezincification; Graphitic Corrosion; 12. STRESS CORROSION CRACKING; Caustic Stress Corrosion Cracking of Carbon Steel; Chloride Stress Corrosion Cracking of Stainless Steel; Ammonia Stress Corrosion Cracking in Copper Alloys; Stress Cracking in Plastics; 13. WELD DECAY AND KNIFE-LINEATTACK IN STAINLESS STEEL; Weld Decay.
|
|
|
:
|
Knife-Line AttackPart III: Corrosion in Water-Bearing Systems; 1. CORROSION IN BOILER SYSTEMS; Corrosion in Feedwater Systems; Water-Side Corrosion in Boilers; Fire-Side Corrosion in Boilers; Corrosion in Steam Systems; Corrosion in Condensate Systems; 2. CORROSION IN WARM AND HOTWATER HEATING SYSTEMS; 3. CORROSION IN COOLING WATERSYSTEMS; Types of Systems; Corrosion Problems in Cooling Water Systems; Corrosion Prevention and Corrosion Control in Cooling Water Systems; 4. CORROSION IN COLD AND HOT TAP WATER SYSTEMS; GLOSSARY OF TERMS USED IN THIS WORK; INFORMATION ABOUT THE MICROPRINTS.
|
|
|
:
|
Prevention3. EXFOLIATION CORROSION; Occurrence; Prevention; 4. FATIGUE AND CORROSION FATIGUE; Influencing Factors; Prevention; 5. FILIFORM CORROSION; Mechanism; Prevention; 6. GALVANIC CORROSION; Conditions for the Occurrence of Galvanic Corrosion; Factors That Can Affect the Rate of Galvanic Corrosion; Forms of Galvanic Corrosion; Prevention; 7. HIGH-TEMPERATURE CORROSION; Carburization; Nitriding; High-Temperature Oxidation; Sulfidation; 8. HYDROGEN DAMAGE; High-Temperature Hydrogen Attack; Hydride Embrittlement; Hydrogen Blistering; Hydrogen Embrittlement; Hydrogen Stress Cracking.
|
| Abstract
|
:
|
Includes 679 case histories divided over 135 materials in 13 material groups, 25 systems (installations) and 44 different phenomena. It is an essential reference work on the design, fabrication, operation and maintenance of the extremely varied and often very complicated systems and machinery used in today's technology. Case histories, with cross-references and indexes, make this book a critical resource in the solution of many corrosion problems. In addition, it brings team members closer by presenting a common language for all parties. Finally, the book serves as an important educational aid for self-study.
|
| Subject
|
:
|
Corrosion and anti-corrosives, Atlases.
|
| Subject
|
:
|
Corrosion and anti-corrosives.
|
| Subject
|
:
|
TECHNOLOGY ENGINEERING-- Engineering (General)
|
| Subject
|
:
|
TECHNOLOGY ENGINEERING-- Reference.
|
| Dewey Classification
|
:
|
620.1/1223
|
| LC Classification
|
:
|
TA467
|
| Added Entry
|
:
|
During, Evert D. D.,1933-
|